金属学报(英文版)
The determination of dffusible hydrogen in U71Mn heavy rail steel,and hydrogen diffusivity as well as the hydrogen distribution in the cross section of blooms with stack cooling were stu- died.The results showed that,most of the hydrogen in blooms of heavv rail steel is diffusible, the hydrogen diffusivity in U71Mn rail steel blooms at room temperature is(0.85—1.02)× 10~(-6)cm~2/s,after stack cooling,the hydrogen content in bloom will decrease greatly which is helpful to form the flake-free phenomenon in the heavy rail produced by Panzhihua Iron and Steel Company.
关键词:
rail steel
,
null
,
null
,
null
FANG Shufang
,
ZHANG Jian Panzhihua Institute of Iron and Steel Research
,
Panzhihua
,
China Laboratory of Physics
,
Panzhihua Institute of Iron and Steel Research
,
Dukou City
,
617000 Sichuan
,
China
金属学报(英文版)
The precipitation of Ti(V)N(C)in high-carbon steel PD_3 during thermomechanicol treatment at austenitic temperatures after deformation has been observed.The average size of Ti(V)N(C)particles may reduce with the increase of strain and the decrease of thermomechanical treatment temperature,and vise versa.The growth of Ti(V)N(C)particles at 920°C is found to be controlled by the interface reaction between precipitated particles and matrix.
关键词:
Ti(V)N(C)
,
null
,
null
XIAN Aiping LI Peiji CHEN Wenxiu WANG Yikang Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
ChinaCHEN Renyi MEI Dongsheng Panzhihua Institute of Iron and Steel Research
,
Panzhihua
,
China associate professor.Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
At panzhihua Iron and Steel Company,hydrogen content in molten heavy rail steel is rather low during smelting in the oxygen top-blown converter,and sloightly increases in tapping and pouring.Average H content varies from 2.0(dry season)to 2.4 ppm(rainy season)at smelt- ing end;2.8 ppm in ladle;and 2.1 ppm(dry season)to 2.3 ppm(rainy season)in mould, which is on a level with RH vacuum circle.The low hydrogen content in molten steel,which is due to both the very dry climate in Panzhiihua region and the LD smelting process,is the main reason why there is little flake in the heavy rail produced by Panzhihua Iron and Steel Com- pany.
关键词:
smelting
,
null
,
null
,
null
,
null