金属学报(英文版)
The dependence of composition varied,especially C,Si,Cr,Cu and Co in four amorphous alloy systems Fe_(80-x)Cr_xSi_5B_(15).Fe_(80-x)Cr_xC_5B_(15).Fe_(80-x)Cu_xSi_5B_(15)and (Fe_(1-x)Co_x)_(82)Cu_(0.4)Si_(4.4)B_(13.2)upon their saturation magnetostriction at room temperature has been studied.It was observed that the saturation magnetostriction of the alloys may be re- markably improved by small addition of Cu and Co.the peak value being up to 70×10~(-6)as x=0.02 in alloys(Fe_(1-x)Co_x)_(82)Cu_(0.4)Si_(4.4)B_(13.2).
关键词:
amorphous alloy
,
null
,
null
By GENG Mingming MA Ruzhang XU Zuxiong WANG Genmiao ** Dept.of Material Physics
,
University of Science and Technology Beijing
,
Beijing
,
100083
,
China*** Structure and Element Analysis Lab.
,
University of Science and Technology of China
,
Hefei
,
230026
,
China+ To w
材料科学技术(英文)
A series of YTi(Fe_(1-x)_(11)alloy with x=0.00,0.01,0.03,0.04,0.05,0.07 and 0.10 has been investigated by measurement of the structural properties and ~(57)Fe M(?)ssbauer experiments.The pure ThMn_(12)-structure phase exists at x≤0.03 and is absent at x>0.03.The reasons for lower satura- tion magnetization and lower energy product of the ThMn_(12)-structure compounds were given.The crystal structure relations between R_2Fe_(17)-structure and ThMn_(12)-structure were discussed.Comparing with the R_2Fe_(17)and R_2Fe_(14)B compounds,the ThMn_(12)-structure RFe_(12-x)M_x compounds have the same magnetic moment of Fe at x=0.The potential for increasing the saturation magnetization of ThMn_(12)-structure compounds may be enhanced by the addition of stabilization elements.
关键词:
ThMn_(12)-structure stability
,
null
,
null
Chimei MO Zaitao LI Dept.of Materials Science and Engineering
,
University of Science and Technology of China
,
Hefei 230026
,
ChinaZhengang ZHU Institute of Solid State Physics
,
Academia Sinica
,
Hefei
,
230031
,
China
材料科学技术(英文)
Effect of solution treatment temperature on transformations and two way memory, effect in a Ti- 55.2 wt-%Ni alloy was investigated. The results show that with increasing the solution treatment temperature (T_s), two way memory effect (TWME) decreases continuously and temperatures of martensite and reverse, martensite transformations (MR) rise, but the temperature of R start trans- formation (parent→R) does not change. The results of the internal friction measurements indicate that when T_s=1073 K, internal friction peaks of MR and P→R transformations are larger than those of the specimens after solution-treatments at 973 and 1173 K. With increasing T_s, the de- crease of TWME can be attributed to that the defect stress field caused by the rolling fades out grad- ually and preferential martensite variants, which fit into the defect stress field, decrease. The changes of transformation temperatures and internal friction peaks with T_s are closely related to the change of defect numbers.
关键词:
solution-treatment temperature
,
null
,
null
,
null
Shihong XU Pengshou XU Mingrong JI Xianming LIU Maosheng MA Jingsheng ZHU Yuheng ZHANG Structure Research Laboratory
,
University of Science and Technology of China
,
Hefei
,
230026
,
ChinaZhenjia XU Institute of Semiconductor
,
Academia Sinica
,
Beijing
,
100083
,
China
材料科学技术(英文)
The alkali-metal Na adsorption on Si(100)2×1 surface and its promoted oxidation and Si oxide growth have been investigated by means of thermal desorption,work function,Auger electron spectroscopy and photoemission electron spectroscopy.The experimental data showed that there was a new state,interface electron state,near the Fermi level after the deposition of Na atoms.It was found that the presence of Na always caused an increase of the oxygen initial uptake whereas the promotion of Si oxide growth was observed only at the coverage of Na greater than 0.5 ML.A new mechanism of Na-promoted Si oxide growth is suggested in this paper.