WANG Kai
,
XU Tingdong
,
SHAO Chong
,
YANG Chun
钢铁研究学报(英文版)
The data obtained by bending tests for intergranular embrittlement after 45 h and 450 h exposure to Strauss solution have been reported for 304 stainless steel. The results show that an embrittlement peak appears at 650 ℃ for all samples quenched from 1260 ℃ and then sensitized for 150 h at 480, 565, 650, 730, 815 and 900 ℃ respectively. The temperature corresponding to the embrittlement peak is decreased to 565 ℃ when the sensitizing time is prolonged to 1500 h. In this paper, these data are analyzed with an isothermal kinetic model of nonequilibrium grain boundary segregation, indicating that the embrittlement peak is related to the critical time for nonequilibrium grain boundary segregation of sulfur.
关键词:
stainless steel
,
intergranular corrosion
,
nonequilibrium segregation
,
grain boundary
,
sulfur
WANG Kai
,
SI Hong
,
YANG Chun
,
XU Tingdong
钢铁研究学报(英文版)
In virtue of Auger electron spectroscopy, the grain-boundary concentrations of phosphorus in Ni-Cr-Fe superalloy after solution-treated at 1180℃ for 45 min are measured, the results show that a peak of phosphorus concentration occurs at about 180 min during isothermal ageing at 500℃, and a maximum concentration of phosphorus appears also at about 500℃ for all specimens aged for 20 min at temperatures of 200,400,500,700 and 800℃. The results are analysed with the laws of non-equilibrium grain-boundary segregation. It is found from the analysis that peaks are relative to critical time for non-equilibrium grain-boundary segregation of phosphorus.
关键词:
Non-equilibrium segregation;Grain boundaries;Phosphorus;Nickel based superalloys