Microstructure and Ferroelectric Properties of (Bi0:9 Ho0:1)3:999Ti2:997V0:003O12 Thin Films Prepared by Sol-gel Method for Nonvolatile Memory

Chengju Fu Zhixiong Huang Jie Li Dongyun Guo

材料科学技术(英文)

The (Bi0.9Ho0.1)3.999Ti 2.997 V0.003O12 (BHTV) films have been prepared on Pt/Ti/SiO2/Si substrates by solgel method. The microstructure and ferroelectric properties of the BHTV films were investigated. The BHTV films show a single phase of Bi-layered Aurivillius structure and dense microstructure. The Ho3+/V5+ cosubstitution can effectively improve the ferroelectric properties. The BHTV film exhibits good ferroelectric properties with 2Pr of 47.6°C/cm2, 2Ec of 265 kV/cm (at applied field of 420 kV/cm), dielectric constant of 305, dielectric loss of 0.031 (at 1 MHz), good insulting behavior, as well as the fatigue-free behavior.

关键词: (Bi0.9Ho0.1)3.999Ti 2.997 V0.003O12 thin films , Sol-gel method , co-substitution , ferroelectric properties , dielectric properties

Nb掺杂Bi4Ti3O12层状结构铁电陶瓷的电行为特性研究

张丽娜 , 李国荣 , 赵苏串 , 郑嘹赢 , 殷庆瑞

无机材料学报

采用固相烧结工艺制备了Nb5+掺杂的Bi4Ti3O12层状结构铁电陶瓷.运用XRD 和AFM对Bi4Ti3-xNbxO12+x/2材料的微观结构进行表征,发现所制备的陶瓷均具有单一的正交相结构,抛光热腐蚀表面晶粒的显微形貌表现为随机排列的棒状结构.通过对材料直流电导率与温度关系的Arrhenius拟合,分析丁Bi4Ti3-xNbxO12+x/2的导电机理. Nb5+掺杂提高了材料的介电常数,但居里温度随掺杂含量的增加呈线性下降趋势.DSC结果显示Bi4Ti3-xNbxO12+x/2材料在居里温度处经历了一级铁电相变.样品的铁电性能测试结果表明, Nb5+掺杂Bi4Ti3O12提高了材料的剩余极化Pr,这主要是由于Nb5+取代Ti4+大大降低了材料中氧空位的浓度,使得氧空位对畴的钉扎作用减弱的缘故.

关键词: 导率 , activation energy , ferroelectric properties , Bi4Ti3O12

LiTa3O8薄膜制备与电性能研究

张德银 , 黄大贵 , 李金华 , 李坤

无机材料学报 doi:10.3724/SP.J.1077.2008.01106

以乙醇锂和乙醇钽为起始反应物, 用溶胶-凝胶法在Pt/Ti/SiO2/Si衬底上制备了新型钽酸锂LiTa3O8铁电薄膜. 经XRD图谱对比, 该薄膜结构不同于LiTaO3晶体结构, 与正交相结构类似. SEM分析显示经过750℃结晶退火的LiTa3O8薄膜表面均匀平整无裂纹, 膜厚约为1μm. 实验结果表明, 在450kV/cm时, LiTa3O8薄膜剩余极化强度Pr为9.3μC/cm2, 矫顽场强Ec为126.8kV/cm; 在9.5kV/cm时, LiTa3O8薄膜漏电电流为8.85×10-9A/cm2, 比LiTaO3薄膜漏电小; 在1kHz时, LiTa3O8薄膜介电常数为58.4, 介电损耗为0.26. 溶胶-凝胶法制备的 LiTa3O8薄膜结晶温度比LiTaO3薄膜高50℃以上.

关键词: 铁电薄膜 , LiTa3O8 , sol-gel , ferroelectric properties , dielectric properties

Li改性铌钽酸钾钠无铅压电陶瓷的研究

江向平 , 胡晓萍 , 江福兰 , 刘晓冬 , 殷庆瑞

无机材料学报 doi:10.3724/SP.J.1077.2007.00465

利用固相反应法制备了(Na 0.52 K 0.48-x Li x)(Nb 0.86 Ta 0.10 Sb 0.04)O 3系无铅压电陶瓷, 研究了不同Li含量(x分别为0、0.02、0.04、0.06、0.08)样品的显微结构、物相组成及电性能. 结果表明, Li含量的改变对其物相组成、压电性能、铁电性能、介电性能都有显著影响. 当Li含量x从0增大到0.04时, 其压电性能相应提高, 当Li含量x超过0.04时, 压电性能明显下降; 在x=0.04时综合性能最好, 其压电常数d33高达260pC/N, 介电损耗tanδ为0.027, 平面机电耦合系数kp值达到50%, 剩余极化强度Pr为22μC·cm-2, 矫顽电场Ec为0.95kV·mm-1, 居里温度为316℃. 另外, 随着Li含量增加, 该系统的矫顽电场明显增强, 居里温度有所提高.

关键词: 铌钽酸钾钠 , lead-free piezoelectric ceramics , piezoelectric properties , ferroelectric properties , dielectric properties

Sb2O3掺杂BNT-BZT1陶瓷的介电和铁电性能

乔辉 , 宋武辉

材料科学与工程学报

采用固相反应法,制备了[0.9 (Bi0.5Na0.5) TiO3-0.1Ba(Ti0.95Zr0.55)O3]+xwt% Sb2O3无铅压电陶瓷,研究了Sb2O3掺杂对样品相结构、介电、铁电性能的影响.实验结果表明:所有样品都形成了纯的钙钛矿结构,无第二相生成.材料存在明显的弛豫现象,从而改善了介电高温温度稳定性(在x=0.6wt%组分、1kHz下、150℃~250℃范围内,介电常数保持在4000左右),但结果同时也表明掺杂使铁电稳定性降低.

关键词: 弛豫性 , 温度稳定性 , 铁电性能