The isothermal oxidation behavior of Ni_3Al containtng 15 at.% Fe and NiAl containing 30 at.% Fe was studied for 100 h at 850, 950, 1050 and 1150℃, respectively. The results show that the oxidation kinetics of the two alloys obey a parabolic law at various temperatures and every parabolic curve possesses two oxidation rate constants. The morphology, microstructure and the chemical composition of the oxide scales were examined using optical metallography, X-ray diffraction analysis, scanning electron microscopy and electron probe microanalysis. The oxide scale of Ni_3Al containing 15 at.% Fe consists mainly of NiO, NiFe_2O_4, and FeAl_2O_4, and that of NiAl containing 30 at.% Fe consists of Fe_2O_3 and (Fe,Ni)Fe_2O_4, contrasting sharply to the oxide scales of pure Ni_3Al and NiAl which consist of Al_2O_3. The oxide scales on the surfaces of Ni_3Al and NiAl containing Fe are not too dense and not too cohesive to the matrix,so their oxidation resistance is not too good.
关键词:
:oxidation
,
null
,
null
,
null
李美栓
,
辛丽
,
马信清
,
彭晓
,
周龙江
,
李铁藩
腐蚀科学与防护技术
利用拉力法测量了Ti-5621S及含1wt%Nd的Ti-5621S合金800℃空气中形成的氧化膜的粘附力,用膜/合金界面能表征的氧化膜的粘附力不仅与断裂载荷有关、而且还与膜内的残余应力有关.简化分析后得出它们间存在关系Ti-5621S合金中添加Nd能增强氧化膜粘附力,两种合金氧化膜的粘附力随厚度增加而降低.
关键词:
氧化
,
oxide adherence
,
residual stress
,
Nd
,
Ti-5621S