Nickel-phosphorus (Ni-P) composite coatings containing potassium titanate (K2Ti6O13) whiskers (PTWs) were prepared by electroless plating. The surface morphology and component of coatings were investigated by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX), respectively before and after wear test. The tribological performance was evaluated using a pin-on-disk wear tester under dry conditions. It is found that the Ni-P-PTWs composite coatings exhibit higher wear resistance than Ni-P and Ni-P-SiC electroless coatings. The favorable effects of PTWs on the tribological properties of the composite coatings are attributed to the super-strong mechanical properties and the specific tunneling structures of PTWs. The PTWs greatly reinforce the structure of the Ni-P-based composite coatings and thereby greatly reduce the adhesive and plough wear of Ni-P-PTWs composite coatings.
关键词:
Potassium titanate whiskers
,
化学镀
,
复合镀层
,
摩擦学性能
宗云
,
郭荣新
,
何冰清
,
刘宏
表面技术
doi:10.3969/j.issn.1001-3660.2009.06.003
为了探索镀液组分对Ni-W-P合金镀层结构与性能的影响规律,寻求合适的镀液配比,为后续实验奠定基础,采用扫描电镜/能谱、X射线衍射以及金相分析等方法,研究了不同成分和结构的化学沉积Ni-W-P合金层,测量了不同成分沉积层的镀态与热处理后的硬度.结果表明:对于Ni-W-P合金镀层,镀液组分是决定镀层结构状态的关键因素.镀液中钨酸钠含量增加,次磷酸钠含量减少时,镀层结构将发生由非晶态→混晶态→纳米晶态的连续演变,其相应的镀态硬度与热处理后硬度也发生变化,这种变化与因成分改变导致的结构、晶化程度、W含量、Ni_3P析出量与尺寸等因素的改变有关.
关键词:
纳米晶
,
化学镀
,
Ni-W-P合金
,
非晶态合金
孙华
,
马洪芳
,
刘科高
,
刘义
表面技术
doi:10.3969/j.issn.1001-3660.2010.01.018
化学镀Ni-P可以改善铝合金易产生晶间腐蚀、表面硬度低、不耐磨损等缺陷,欲使镀层与铝合金基体具有很好的结合力,前处理工艺则显得尤为重要.采用正交试验,用极差法分析了活化和预镀镍各工艺参数对后续化学镀Ni-P镀速影响的主次顺序,确定了活化和预镀镍镀液的最佳配方及各工艺条件,并利用金相显微镜、扫描电镜能谱、增重法、热震实验和失重法等测试了采用最佳活化、预镀镍工艺所得镀层的形貌和性能,结果表明:所确定的活化、预化学镀镍前处理工艺可显著提高镀层的硬度、沉积速率及其与基体的结合强度,镀层组织致密均匀,耐蚀性优良.
关键词:
化学镀
,
Ni-P合金
,
沉积速率
,
镀层性能
,
活化-预化学镀
,
预镀镍
张海军
,
赵国刚
,
周月波
表面技术
doi:10.3969/j.issn.1001-3660.2009.06.004
为了更深地认识CNTs对Ni-P镀层电化学腐蚀性能的影响,采用复合化学镀技术,通过向优化的化学镀溶液中加入碳纳米管的方法在45~#钢基材上制备了Ni-P-CNTs复合镀层,并用相同工艺在45~#钢基材上直接化学镀Ni-P镀层作为对比.采用SEM/EDAX,XRD和TEM综合分析了复合镀层的形貌和结构,分析表明:所得镀层t,X非晶结构为主,碳纳米管均匀分布在镀层中.采用动电位极化及交流阻抗技术对比研究了Ni-P-CNTs复合镀层及纯Ni-P镀层在0.5mol/L NaCl+0.05mol/L H_2SO_4酸性溶液中的电化学腐蚀行为,腐蚀实验结果表明:在该介质溶液中,与不含碳纳米管的Ni-P镀层相比,Ni-P-CNTs复合镀层的自腐蚀电位和自腐蚀电流密度较低,耐均匀腐蚀性能得到明显改善;此外,碳纳米管的加入还明显提高了Ni-P镀层在该介质溶液中的耐点蚀性能.
关键词:
碳纳米管
,
化学镀
,
Ni-P镀层
,
酸性介质
,
腐蚀
胡庆华
,
王玺堂
,
陈浩
,
王周福
新型炭材料
doi:10.1016/S1872-5805(12)60003-1
采用化学镀镍方法,以氧化石墨烯薄片为基体、NaBH4为还原剂,在NiSO4溶液中制备了Ni/石墨烯.通过X射线衍射、场发射扫描电镜和透射电镜对样品进行了表征,结果表明:沉积在石墨烯片表面Ni的的质量分数高达32.9％时,仍具有高度的分散性；相互堆积Ni/石墨烯片形成了介孔和大孔.氮气等温吸附表明:其介孔和大孔为狭缝型结构,孔的Brunauer-Emmett-Teller比表面积为91 m2/g;吸附支的Barret-Joyner-Halenda平均孔径为3.83nm,孔容为0.28 cm3/g.
关键词:
化学镀
,
石墨烯
,
氧化石墨烯
,
介孔
,
大孔
肇研
,
薛亚娟
,
郑浩
,
段跃新
新型炭材料
doi:10.1016/S1872-5805(09)60016-0
采用化学镀法在多壁碳纳米管表面沉积钴-铁涂层.主要研究了镀液中钴盐和铁盐的摩尔比、络合剂浓度和镀液温度对镀层的影响.在钴-铁的摩尔比为9:1,络合剂浓度为0.32 mol/L,镀液温度为60 ℃时,可得到的较为平整的镀层,且镀层中钴-铁摩尔之和达90%以上.其他条件下,则会在镀层中出现金属颗粒或钴-铁含量过少的情况.
关键词:
多壁碳纳米管
,
钴
,
铁
,
化学镀
,
络合剂
张欣欣
,
齐暑华
,
钟晓兰
,
何征
,
邱华
宇航材料工艺
通过对Fe3O4化学镀Ag,提高其电导率,从而获得电磁性能优异的复合材料.进行化学镀之前,要对Fe3O4进行包括粗化、敏化和活化等预处理.测试结果表明:Fe3O4表面成功包覆一层Ag,厚度大约为25～100 nm,Ag含量达到54.47％;Ag/Fe3O4的电导率σ=347.15 S/cm,相比Fe3 O4升高了9个数量级,饱和磁化强度Ms=29.8 emu/g.
关键词:
Fe3O4
,
化学镀
,
Ag/Fe3O4
,
电磁性能
崔海萍
,
闫军
,
王彬
,
杜仕国
表面技术
doi:10.3969/j.issn.1001-3660.2009.06.020
为了使PVC材料具备电磁屏蔽性能,利用化学镀工艺在PVC基材表面制备了Ni-Co-P合金镀层.利用网络分析仪测量法对镀层的电磁屏蔽效能进行测试,研究了不同沉积时间和钴盐含量对合金镀层电磁屏蔽性能的影响.结果表明:随着沉积时间的增加,镀层电磁屏蔽效能逐渐增加,当沉积时间超过60min之后,镀层的电磁屏蔽效能增加不再明显;而硫酸钴含量的变化对镀层电磁屏蔽效能的影响不明显,这可能是由于钴比镍难还原,含钴镀层的形成比较缓慢,当沉积时间一定时,改变镀液中硫酸钴的含量对镀层沉积速度影响不大所致.
关键词:
化学镀
,
Ni-Co-P合金
,
PVC
,
电磁屏蔽效能