The distribution of microelement Fe, Si, Cu and Mg in the surface layer of aluminum foil annealed at 300℃ and 500℃ were determined by secondary ion mass spectrometer. The corrosion structure produced by electrochemical etching was also observed. It was found that the Mg concentration at external surface was increased exponentially over the fourth degree and promoted by higher annealing temperature, which will increase the number of corrosion pits inside the large grains, and therefore the specific capacity of the foils for electrolytic capacitors. The similar effects of microelement Fe, Si and Cu were not so strong.
关键词:
Electrolytic capacitor
,
null
,
null
,
null
Jingbo SONG
,
Weimin MAO
材料科学技术（英文）
The effect of trace Sn on the pitting morphology of high voltage anode aluminum foils was investigated. The distributions of microelement Sn, Fe, Si, Cu and Mg in the surface layer of aluminum foils with different Sn content were determined by using a secondary ion mass spectrometer. It was found that the micro-alloyed Sn is enriched at the external surface. The mechanism of pitting behavior of trace Sn on aluminum surface is similar with that of lead. Enrichment of Sn in the surface layer provides large numbers of sites for initiation of pitting corrosion, while pitting sites appeared relatively inhomogenously in the foils without Sn. Sn, as an eco-friendly microelement, can be applied to replace Pb in improving the homogenous pitting behaviors of high voltage aluminum foils, in which the volume fraction of cube texture is not reduced.
关键词:
Electrolytic capacitor
,
铝箔
,
锡
,
孔腐蚀