TRANSFORMATION OF Nd_(14)Fe_(73)Co_6B_7 ALLOY UNDER HYDROGEN TREATMENT

LIU Jian QIU Baoqin LIU Muyi XIAO Yaofu University of Science and Technology Beijing , Beijing , China associate professor , Department of Materials , University of Science and Technology Beijing , Beijing 100083 , China

金属学报(英文版)

The phase constitution and variation of Nd_(14)Fe_(73)Co_6B_7 alloy after hydriding and subsequent dehydriding treatment at 770℃ have been investigated respectively by means of X-ray diffraction,SEM,TEM and magnetic measurement techniques.The original coarse,as cast grain structure,is dissolved into α-Fe,Nd hydride and Fe_2B mixture with average dimension of 0.1 μm,during hydriding process,and subsequently the triphase mixture recombined into finely unique Nd_2Fe_(14)B phase with dimension of 0.3 μm by desorbing the hydrogen.It was found that the Nd-rich phase distributed at the boundary of as-cast grain structure diffused into matrix Nd_2Fe_(14)B grain during hydriding.It remains during dehydriding and distribute homogeneously around some colonies composed of fine grains of Nd_2Fe_(14)B.

关键词: Nd_(14)Fe_(73)Co_6B_7 , null , null , null

氢作用下Nd_(14)Fe_(73)Co_6B_7的相转变

刘俭 , 裘宝琴 , 刘慕怡 , 肖耀福

金属学报

利用X射线衍射、透射电子显微镜、扫描电镜及磁测量技术观察和分析了Nd_(14)Fe_(73)Co_6B_7合金于770℃吸氢后相结构组成与变化发现铸锭中的Nd_2Fe_(14)B基体吸氢后分解成约为0.1μm的NdH_2,α-Fe和Fe_2B三相混合物,脱氢后重新结合的Nd_2Fe_(14)B相尺寸约为0.3μm;铸锭中分布在基体相周围的富Nd边界相在吸氢时扩散入Nd_2Fe_(14)B基体,在脱氢过程中保留下来,均匀地分布在由若干Nd_2Fe_(14)B细小晶粒组成的晶粒团周围

关键词: Nd_(14)Fe_(73)Co_6B_7合金 , Nd-rich phase , transformation , hydriding