Three high-nitrogen stainless steels with different N contents were successfully processed by equal-channel angular pressing for one pass, and their microstructures and mechanical properties were investigated. It was found that the microstructure of the billet was heterogeneous across the billet thickness, resulting in the difference in the mechanical properties due to the different deformation conditions. A relatively low strength, high uniform elongation, and high work-hardening rate for the samples at the bottom of the billet was achieved in comparison with those processed at the top. Meanwhile, it was observed that the density of deformation twins increased with the content of N; accordingly, the strength and elongation of the alloys increase with the content of N, resulting in a good strength-ductility combination.
关键词:
High-nitrogen
,
stainless
,
(HNS)
,
steels
,
Equal-channel
,
angular
,
pressing
,
(ECAP)
,
N
,
content
,
Twinning
,
Strength
,
Ductility
涂元强
,
柳长福
,
白会平
,
蔡捷
,
郭玉华
钢铁研究
通过采用扫描电镜(SEM)、酸浸时滞试验、合金-锡电偶试验等仪器,对研制的MR T-2.5BA耐腐蚀软质镀锡板性能进行了检测与分析,结果表明:MR T-2.5BA镀锡板具有优良的耐蚀及冲压成形性能,各项性能(镀锡量、硬度值、PL值、ATC值等)均达到《GB/T2520-2008》规定的指标;试制产品经用户试用,其性能满足制作各种耐蚀罐要求。
关键词:
耐腐蚀
,
冲压成形
,
软质镀锡板