The influence of rare-earth elements,La,Ce,Pr,Nd,Sm,Eu,Gd,Dy,Ho,Er and Yb on the thermal stability of PdSi_(16.5) glass was studied systematically by means of DSC.All rare-earth elements,especially heavy ones,increase obviously the thermal stability parameters,including T_θ(T_g ,T_x ,T_g),T_(rg) and ΔE etc.The crystallization temperatures T_(p1) and T_(p2) increase linearly with the lanthanide constriction increasing,but Eu shows an anomalous influence:Pd-Si-Eu metallic glass possesses the highest thermal stability and the lowest concentration limit of glass forming among Pd-Si-R glasses.
关键词:
thermal stability
,
null
,
null
,
null
傅绪鑫
,
单爱党
,
周灿栋
,
宋洪伟
机械工程材料
利用Gleeble-3800热模拟试验机、光学显微镜、扫描电镜和能谱仪等研究了稀土元素铈对铸态00Cr25Ni7Mo4N超级双相不锈钢在应变速率为5 s-1、变形温度为1 100,1 150,1 200℃下热变形行为的影响.结果表明:稀土元素铈能够降低该钢中氧、硫含量,使钢中的夹杂物由硫化物变成稀土夹杂物,从而在一定程度上改善了该钢的热变形能力;铈的较佳添加量为0.165%～0.220%,适宜的热变形温度为1 150～1 200℃.
关键词:
双相不锈钢
,
稀土元素
,
铈
,
热变形
,
夹杂物
王定刚
,
肖程波
,
宋尽霞
,
李青
,
余乾
材料工程
doi:10.11868/j.issn.1001-4381.2014.08.009
利用金相技术和扫描电镜(SEM)观察分析了稀土元素(Ce+Y)含量对K465合金微观组织的影响,并测试了合金的室温瞬时拉伸性能和高温持久性能.结果表明:(Ce+Y)含量为0.03％(质量分数,下同)的合金碳化物变质处理后形态良好,高温持久性能大幅提高;(Ce+Y)含量为0.06％的合金枝晶间区大块γ'目的边缘析出富(Ce+Y)相,从而使合金的持久性能明显下降.
关键词:
K465合金
,
稀土元素
,
微观组织
,
力学性能