Lianbang Wang Guobin Wu Zhenzhen Yang Yunfang Gao Xinbiao Mao Chun'an May
材料科学技术（英）
Fuel cells using borohydride as the fuel have received much attention because of high energy density and theoretical working potential. In this work, LaNi4.5Al0.5 hydrogen storage alloy used as the anodic material has been investigated. It was found that the increasing operation temperature was helpful to the open-circuit potential, the discharge potential and the power density, but showed a negative effect on the utilization of the fuel due to the accelerated hydrogen evolution. The high KOH concentration was favorable for high-rate discharge capability. The adsorption and transformation of hydrogen on LaNi4.5Al0.5 alloy electrode has been observed, but its contribution to the discharge capability during a high-rate discharge was small.
关键词:
Fuel cell
,
硼氢化物
,
阳极催化剂
,
储氢合金
Lianbang Wang Guobin Wu Zhenzhen Yang Yunfang Gao Xinbiao Mao Chun'an May
材料科学技术（英）
Fuel cells using borohydride as the fuel have received much attention because of high energy density and theoretical working potential. In this work, LaNi4.5Al0.5 hydrogen storage alloy used as the anodic material has been investigated. It was found that the increasing operation temperature was helpful to the open-circuit potential, the discharge potential and the power density, but showed a negative effect on the utilization of the fuel due to the accelerated hydrogen evolution. The high KOH concentration was favorable for high-rate discharge capability. The adsorption and transformation of hydrogen on LaNi4.5Al0.5 alloy electrode has been observed, but its contribution to the discharge capability during a high-rate discharge was small.
关键词:
Fuel cell
,
硼氢化物
,
阳极催化剂
,
储氢合金
唐睿
,
张朝晖
,
刘丽琴
,
朱杰武
,
柳永宁
中国有色金属学报
采用XRD分析了La1.3CaMg0.7Ni9储氢合金的晶体结构,并研究了合金的气相储氢特性以及电化学性能.结果表明,合金由具有PuNi3结构的LaNi3主相和LaNi5、LaNi2.28第二相构成;在1.6MPa氢压和300K下,合金的储氢量达到1.68%(质量分数),比纯LaNi5的储氢量提高了20%;合金的活化性能良好,经3个充放电循环即可完全活化,其放电容量达到395mA*h/g,比AB5型储氢合金的容量提高了23%,经100次循环后容量保持率为80%.
关键词:
储氢合金
,
P-C-T曲线
,
放电容量
,
循环稳定性
黄太仲
,
吴铸
,
余学斌
,
陈金舟
,
夏保佳
,
徐乃欣
稀有金属
doi:10.3969/j.issn.0258-7076.2004.04.032
由Ti-Cr基合金的二元相图出发,综述了Ti-Cr基合金的储氢性能,并重点介绍了多元合金化对其储氢性能的影响.合金TiCr1.8中存在BCC和Laves相,吸氢量随温度的升高而有所下降.Zr取代合金中的部分Ti使合金的晶胞参数增大,同时合金的吸氢量增加,平台压力降低,平台区变短.V取代合金中的部分Cr也使合金的吸氢量增加,吸放氢过程中的滞后效应增加.Fe,Mn,Cu,Ni对合金的性能也有一定影响.相同的退火时间下,TiCrV合金的吸氢量随退火温度的升高而增加.
关键词:
Ti-Cr基合金
,
储氢合金
,
相图
,
退火
刘剑
,
陈立新
,
郑坊平
,
代发帮
,
陈长聘
稀有金属材料与工程
系统研究了Zr含量对(Ti-Cr)45-xV55Zrx(x=1,3,5,7;Ti/Cr=0.7～0.75)合金微结构及储氢性能的影响.XRD及SEM分析表明,当Zr含量x=1时,合金由体心立方(bcc)结构的钒基固溶体主相和微量α-Zr第二相组成;当Zr含量增至x=3～7时,合金由bcc钒基固溶体主相和α-ZrCr2第二相组成.储氢性能测试表明,随着Zr含量的增加,合金的活化性能得到改善;室温最大吸氢量和80℃有效放氢容量均先增后降,并在x=5时达到最高值;P-C-T曲线滞后减小,平台倾斜度增大.在所研究的合金中,(Ti-Cr)40V55Zr5合金的综合性能最佳,经2次吸放氢循环就活化,室温最大吸氢量可达403 ml/g,80℃有效放氢容量达到230 ml/g.
关键词:
储氢合金
,
钒基固溶体
,
bcc结构
,
储氢性能
唐睿
,
刘丽琴
,
柳永宁
,
于光
,
朱杰武
,
刘晓东
中国有色金属学报
通过感应容炼制备了La0.8-xREMg0.2Ni3.2Co0.6(RE=Sm,Dy,0≤x≤0.3)合金.采用X射线衍射分析了该合金的晶体结构,并研究了其电化学性能.结果表明:该合金是由LaNi5主相和LaNi3第二相构成;随着Sm(Dy)取代La量的增加,合金主相单胞体积线性收缩,合金储氢量和放电容量减小,当Sm(Dy)取代量分别为0.1、0.2、0.3时,合金容量由380 mA·h/g分别减小到370(362)、355(334)、329(295)mA·h/g,但高倍率放电能力和循环稳定性得到改善,100次循环后的容量损失率由20%分别降低到18%(17%)、16%(14%)、13%(11%).
关键词:
镍氢电池
,
储氢合金
,
稀土
,
放电容量
姜锋
,
张喜燕
,
齐琳琳
,
赵敏
,
黎学勤
,
周世杰
,
高界铭
材料导报
综述了近年来镁基材料合金化研究的状况,分别介绍了镁基结构材料、储氢合金、非晶合金等方面合金化研究的最新进展.最后,对镁基材料的其它研究领域做了简要地说明.
关键词:
镁
,
合金化
,
结构材料
,
储氢合金
,
非晶合金
李汉军
,
孙杰
,
何国荣
,
吴锋
材料导报
从储氢合金的研究分类,采用的技术手段等方面,综述了MH-Ni电池负极用储氢合金的研究与发展.详细论述了AB5型和AB2型储氢合金的研究进展,并对储氮合金的未来发展方向进行了展望.
关键词:
镍氢电池
,
储氢合金
,
动力
,
电动车
刘静
,
赵显久
,
张旭
,
李谦
,
林根文
,
周国治
稀有金属材料与工程
采用熔盐保护熔炼法(SMPMS)成功制备了La2Mg17储氢合金.SEM和EDS研究发现,熔炼时液相在凝固过程中形成微观成分不均匀的非平衡组织.通过PCT性能测试发现,合金在523～623 K时可逆吸放氢量大于4.3%(质量分数, 下同).动力学分析结果表明,合金在473～623 K时具备良好的氢化动力学性能,并且在523 K时出现氢化速率极大值(25 s内吸氢3.2%).丰富的表面裂纹改善了合金的储放氢性能.
关键词:
熔盐保护熔炼法
,
储氢合金
,
La2Mg17
,
性能
唐睿
,
刘丽琴
,
柳永宁
,
于光
中国有色金属学报
研究了储氢合金 (MlMg)Ni4-xCo0.7Znx (0≤x≤0.3) 的气相储氢特性和电化学性能.结果表明,随着Zn含量的增加,合金吸、放氢 (室温下) 的平台压力降低,最大储氢量减少,分别从1.58% (x=0) 减少到1.44% (x=0.2)、1.19% (x=0.3);合金的放电容量减少,分别从380 mAh/g (x=0) 减少到366 mAh/g (x=0.1)、345 mAh/g (x=0.2)、271 mAh/g (x=0.3),但循环稳定性得到提高,经100次充放电循环后的容量衰减率从16% (x=0) 降低到4% (x=0.3);适当控制Zn含量,既对合金的放电容量无大的影响,又可提高合金放电的稳定性,尤其是在大电流下放电的稳定性.
关键词:
储氢合金
,
P-C-T曲线
,
放电容量
,
循环稳定性