Haifei YAO
,
Jialin SUN
,
Wei LIU
,
Hongsan SUN
材料科学技术（英）
The effect of an external magnetic field on the preparation of silver nanowires was studied. The silver nanowires were synthesized using solid electrolyte RbAg4I5 thin films by applying both a direct current (DC) electric field and a magnetic field. The RbAg4I5 thin films, which were prepared by deposition at room temperature and atmospheric pressure on a NaCl substrate, were used for the transfer of Ag+ ions between two Ag electrodes during the preparation process. When only the DC electric field is applied, the silver ions migrate toward the cathode. On the edge of the silver film at the cathode the Ag+ ions congregate to form aligned nanowires. If the magnetic field is also applied perpendicular to the DC electric field, the morphology of the nanowires can be controlled by rotating the sample in the magnetic field. Experimental results show that the growth of the silver nanowires is determined by the Ag+ ionic flux.
关键词:
Silver nanowires
,
固体电解质
,
磁场
高运明
,
阮栋
,
杨映斌
,
段超
材料与冶金学报
doi:10.14186/j.cnki.1671-6620.2015.02.008
电解含有铁氧化物的熔渣是一个潜在的减少甚至消除CO2排放的钢铁冶炼短流程新工艺.本文采用MgO或Y2O3稳定的氧化锆管内装碳饱和铁熔体做阳极,构建可控氧流电池:铁棒｜ Fe+ FeO(slag)｜ ZrO2(MgO或Y2 O3)｜[O](Fe+c饱和)｜石墨棒.在1723 K高温下通过测定电池开路电压-时间曲线、线性扫描伏安曲线、恒电压电解曲线研究了SiO2-CaO-Al2O3-MgO-FeO熔渣的电解还原行为,并借助扫描电镜与能谱分析了残样的显微结构与成分.结果表明:在本实验条件下,测定获得SiO2-CaO-Al2 O3-MgO-FeO熔渣中FeO的分解电压约为-0.25 V,测定结果位于FactSage热力学软件理论计算值范围内,表明采用本实验装置测定熔渣中FeO分解电压是可行的.在外加电压条件下可以从SiO2-CaO-Al2 O3-MgO-FeO熔渣中电解还原获得金属铁(或铁合金).可控氧流电解还原电流的大小及FeO还原效果与外加电压、ZrO2稳定剂的种类和ZrO2管(阳极)插入熔渣中的深度等因素有关.
关键词:
SiO2-CaO-Al2O3-MgO-FeO渣
,
电解还原
,
可控氧流
,
分解电压
,
固体电解质
陈启元
,
曾晓国
,
刘常青
,
尹周澜
,
张平民
稀土
doi:10.3969/j.issn.1004-0277.2008.03.006
以乙二醇为溶剂,柠檬酸为络合剂,用溶胶凝胶-自蔓延燃烧法合成La1-xSrxMnO3纳米粉体.探讨了制备过程中的最佳成胶温度,pH值,烧结温度;利用X衍射分析了掺锶量对晶体结构的影响;用数字电桥测定了不同掺锶量的样品的电导率;运用热重和红外光谱对粉体的形成过程进行了分析.实验结果表明,最佳制备条件是:成胶温度65℃,溶液初始pH值1.5,烧结温度800℃;粉体的电导率随掺锶量增加而增大,以x=0.3最大;自燃烧后La1-xSrxMnO3钙钛矿结构已初步形成且掺杂后钙钛矿结构没有改变,但晶胞参数发生了一定的变化.
关键词:
固体电解质
,
柠檬酸
,
溶胶凝胶-自燃烧
,
La1-xSrxMnO3
,
电导率
周德凤
,
叶俊峰
,
朱建新
,
孟健
功能材料
以La2Mo1.7W0.3O9为本体,在La位进行碱土金属掺杂,采用溶胶-凝胶方法合成新型氧离子导体La1.84R0.16Mo1.7 W0.3O8.92(R=Ca2+、Sr2+、Ba2+).应用示差热分析(DTA)、X射线衍射(XRD)、拉曼光谱(Raman)等手段对氧化物进行结构表征,交流阻抗谱测试电性能.结果表明:掺杂改善了本体导电性能的同时,保持了La2Mo1.7W0.3O9抑制La2Mo2O9相变的功能;碱土离子的掺杂,在体系中引入了氧空位,有利于氧离子扩散,提高氧离子导电性,773K时Ba2+掺杂体系的电导率为1.0×10-4S/cm,高于本体的电导率(5.0×10-5/cm).
关键词:
固体电解质
,
氧离子导体
,
掺杂
,
La2Mo2O9
李彬
,
潘伟
,
陈争辉
,
刘燕祎
稀有金属材料与工程
通过X射线衍射,DSC和交流阻抗等测试方法研究了镉掺杂Bi2VO5.5的结构,相变和电性能.由于Cd2+的半径与V5+和Bi3+的半径都比较接近,所以在合成BICDVOX体系时假设了两种模型:Bi2V1-xCdxO5.5-3/2x(x=0.05,0.075,0.10,0.125,0.15)和Bi2-xVCdxO5.5-1/2x (x=0.10,0.20).XRD和DSC分析表明了这两种模型可能同时存在.根据交流阻抗谱的结果,当x=0.10时,具有较高的电导率,这归因于此成分使高电导的四方相可以稳定到室温.
关键词:
镉掺杂
,
Bi2VO5.5
,
电导率
,
相变
,
固体电解质
赵沁
,
王新平
,
蔡天锡
催化学报
综述了近年来利用固体电解质电解池消除NO的研究进展. 重点总结了电化学消除NO研究体系、电化学消除NO分解机制、O2-在固体电解质电解池中传导的控速步骤、电极种类和形态对NO分解性能的影响以及直流与交流电作用的差异等几个方面的研究结果. 在RuO2︱Ag︱YSZ︱Pd电解池上实现的NO选择性分解是迄今为止的最佳结果,500 ℃下NO的转化率为31.8%,NO的分解活性是O2的分解活性的13倍. 该领域今后研究的主要方向是,进一步提高NO分解相对于共存O2离子化的选择性、降低O2-在阴极界面处的传导阻力和探寻可在更低温度传导O2-的新的固体电解质.
关键词:
氧化氮
,
分解
,
电化学消除
,
固体电解质
孟波
,
谭小耀
,
杨乃涛
,
张宝砚
中国有色金属学报
采用基于Pechini法的低温燃烧工艺制备了SrCe0.95Y0.05O3-x(SCY)前驱物.前驱物在900℃经0.5 h的煅烧处理即可得到纯的粒度在7～25 nm范围内的SrCe0.95Y0.05O3-x固体电解质纳米粉.将煅烧的粉体在18 MPa压力下压成片状的素坯,在900～1 500℃的温度范围内于空气中烧结索坯10 h.用X射线衍射(XRD)表征煅烧粉体的晶体结构,用扫描电镜(SEM)和透射电镜(TEM)表征了煅烧粉体和烧结体的形貌和粒度,采用阿基米德法测量了烧结体的密度.结果表明:温度达到1 000℃时,烧结体的径向收缩率和密度随着温度的升高而显著增加;温度达1 300℃时烧结体的径向收缩率和密度趋于恒定,得到相对密度高于96%、平均粒径约为3.68 μm的SrCe095Y0.05O3-x固体电解质陶瓷体.
关键词:
固体电解质
,
SrCe0.95Y0.05O3-x
,
纳米陶瓷粉
,
烧结
,
低温燃烧
吕振刚
,
郭瑞松
,
姚琲
,
代凤英
稀有金属材料与工程
采用高温固溶法制备Sc2O3(Dy2O3)和Yb2O3复合掺杂YSZ电解质材料,研究了复合掺杂对YSZ烧结性和电性能的影响.结果表明:随着Sc2O3含量的增加,试样烧结密度降低(1600℃烧结密度由5.82g/cm3降至5.24g/cm3),而Dy2O3却能提高烧结密度(1600℃烧结密度由5.63g/cm3增至5.86g/cm3);当掺杂总量(x,%)为8～8.6时,材料电导率得到大幅度提高(1000℃时,0.18 S/cm);lnσ-1000/T呈现较好的线性关系,说明电导率σ与温度T之间关系符合Arrhenius 公式;XRD分析表明复合掺杂YSZ电解质材料晶格常数有所增大,对提高电导率起积极作用;复合添加剂促进了晶粒生长,尤其是含Dy试样晶粒尺寸较大.
关键词:
固体电解质
,
导电性
,
烧结性
,
复合掺杂剂